Product Details:
Grade | Industrial Grade |
Packaging Size | 25 kg |
Color | White |
Packaging Type | Bag |
Country of Origin | Made in India |
Raw Material | Talc powder |
Form | Powder |
Characterstics | Requirements | Observations |
Magnesium (as mgo)% by weight min. | 20 | 14.25% |
Acid Soluble Matter %by mass max. | 6 | 4.91 |
Brightness | 88.00% | Test passes |
Mesh | 300 | Test passes |
Product Details:
Form | Cut-to-Size |
Usage/Application | Commmecial |
Size | Lumps |
Usage | Boiler |
Color | White, Grey |
Country of Origin | Made in India |
Product Details:
Physical State | Powder |
Usage/Application | Industrial |
Country of Origin | Made in India |
Layer | 25 mm |
Application | APC |
Raw Material | Anti Piping Compound |
Product Details:
Form | Powder |
Usage/Application | Industrial |
Country of Origin | Made in India |
Caso3 | 40 % to 56 5 |
Mgco3 | 34 % to 43 5 |
Silica | 1.05% |
Cao | 31.08 5% |
Mgo | 20.10% |
Product Details:
Form | Powder |
Country of Origin | Made in India |
MgO | 44-48 % |
Al 203 | 0, 1 % |
Fe 203 | 0, 2 % |
CaO | 1, 5 % |
SiO2 | 6 % |
Product Details:
Usage/Application | Foundry |
Packaging Type | Bag |
State | Powder |
Country of Origin | Made in India |
Silica Percentage Varies | From 98 to 99 % |
Recommended | Up to 1600 degree |
It is basically used in small capacity induction and cupola furnaces & is lesser resistant to high temperature. Recommended up to 1600 degree. The silica percentage varies from 98 to 99%.
Product Details:
Purity % | 98% |
Grade Standard | Lab Grade |
Form | Powder |
Packaging Type | Bag |
Packaging Size | 50 Bag |
Usage | Commercial |
Test | Unit | Result |
B2O3 | %, min | 56.25 |
Purity | %, min | 99.9 |
So4 | ppm, max | 500 |
Cl | ppm, max | 15 |
Fe | ppm, max | 20 |
Product Details:
Packaging Type | Bag |
Color | White |
Usage/Application | Industrial |
Country of Origin | Made in India |
State | Powder |
Purity | 68 % |
Product Details:
Machine Type | Foundry Chaplet |
Surface Finish | Powder Coated |
Country of Origin | Made in India |
Material | Steel |
Application | For casting |
Technique | Casting |
Product Details:
Packaging Type | Customized |
Usage/Application | Drilling |
Country of Origin | Made in India |
Form | Powder |
Seive anlysis (Wet)- 202 Mesh | 98 % Min. |
Gelling time (10 % ) | Instantaneous |
Physical Properties | Foundry Grade | Alka Bond | Superior Grade |
Moisture (@105 degree-110 degree C | 13 % Max. | 13 % Max. | 13 % Max. |
Seive anlysis (Wet)- 202 Mesh | 98 % Min. | 98 % Min. | 98 % Min. |
PH (6 % Suspension) | 8.8- 9.5 | 9.2- 9.8 | - |
Swelling capacity (2gms/ 100cc) | 25 Min. | 28 Min. | - |
Gelling time (10 % ) | Instantaneous | Instantaneous | Instantaneous |
MB Value (MG/GM of Bentonite) | 370 Min. | 400 Min. | 420 Min. |
Gel formation inex | 55 Min. | 70 Min. | 80 Min. |
Thermal stability | - | - | 50 % Min. |